Flame Retardant OP1312 OP1314 for PA6 PA66

$8000

≥1
Metric Ton

option:

P (as P2O5) content, % :18-21
Decomposition Temperature, °C : ≥350
Average particle size, um: D50≤10

Contact Now

 Chat Now

Product Description

Product Attributes
Supply Ability & Additional Information
Packaging & Delivery

< >

Overview

Product Attributes

Model No.: PN2131CG

Brand: Novista

Place Of Origin: China

Appearance: Powder Or Granule

Color: White

Supply Ability & Additional Information

Packaging: 25kg/bag

Productivity: 3,000MT

Transportation: Ocean,Land,Air

Place of Origin: China

Supply Ability: 3,000MT

Certificate: REACH/ROHS

HS Code: 382499999

Port: QingDao,Shanghai

Payment Type: L/C,T/T,D/P

Incoterm: FOB,CFR,CIF

Packaging & Delivery

Selling Units:: Metric Ton

Package Type:: 25kg/bag

Halogen free Flame Retardant PN2131CG Used for PA6/PA66+ Glass fibre

ProFlame-PN2131CG is formulated flame retardant based on organic phosphorus component. It is suited for both GF-reinforced PA6/PA66 system. The polyamide compounds exhibit very good physical and electrical properties with PN2131CG. It is flame retardant plasticizer mixture of columned granule and powder, this will be helpful to reduce dust ,and make material easy to dispersing and feeding.

Technical Data:

Items Spec
Appearance                                                White free-flowing powder/columned granule
P (as P2O5) content, %                                                               18-21
Decomposition Temperature, °C   ≥350
Average particle size, um D50≤10
Moisture,% ≤0.5
Whiteness    ≥95

Recommended dosage:

Polymer	PN2131CG	UL-94	GWFI
20-30%GF-Reinforced PA6	15-18	V0(0.75-1.6mm)	960°C
20-30%GF-Reinforced PA66	15-18	V0(0.75-1.6mm)	960°C

Processing instruction:
1. Pre-drying the polyamide,the moisture content should be below 0.1 % (by wt.).

2. The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components.

3. The temperature of the polymer melt should not exceed 350 °C.

4. It is most suitable for equipment with weak shear force.

5. The processing temperature of Parallel twin-screw extruder should keep between 210 ~ 245 ℃ with vacuum at the same time.The temperature is too high, the physical property loss of PA6 is large, and the yellowing is also large.

6. Do not use low-alkali or high-alkali fiberglass. High-quality non-alkali fiberglass is preferred.

Package & Storage:
Net weight 25KG Kraft bag with PE liner.
Minimum shelf life is 12 months stored in a dry and ventilated warehouse.

Product Categories : Flame Retardant > Halogen-Free Flame Retardant

Hot Products