Product Description

Product Attributes
Supply Ability & Additional Information
Packaging & Delivery

< >

Overview

Product Attributes

Model No.: PN2131C

Brand: NOVISTA

Supply Ability & Additional Information

Packaging: 25kg/bag

Productivity: 3,000 MT

Transportation: Ocean,Land,Air

Place of Origin: CHINA

Supply Ability: 3,000 MT

Certificate: ROHS/SGS

HS Code: 3824999990

Port: Qingdao

Payment Type: L/C,T/T,D/P

Incoterm: FOB,CFR,CIF

Packaging & Delivery

Selling Units:: Bag/Bags

Package Type:: 25kg/bag

ProFlame-PN2131C/CD is formulated flame retardant based on organic phosphorus component. It is suited for both GF-reinforced and unreinforced PA6/PA66 system. The polyamide compounds exhibit very good physical and electrical properties with PN2131C.

Technical Data: Items Spec

Appearance White free-flowing powder

P (as P2O5) content, % 18-21

1% TGA Temperature, °C ≥320

Average particle size, um D50≤15

PH value 4.5-6.5

Moisture,% ≤0.5

Solubility in water %, 25°C , g/100mL H2O ≤0.5

Whiteness ≥97

Recommended dosage:

Polymer	PA6	PA66	UL-94	GWFI
Unreinforced	17-20	15-18	V0(1.6mm)	960°C
20-30%GF-Reinforced	14-17	12-16	V0(1.6mm)	960°C

Processing instruction:

1. Pre-drying the polyamide,the moisture content should be below 0.1 % (by wt.).

2. The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components.

3. The temperature of the polymer melt should not exceed 320 °C.

4. It is most suitable for equipment with weak shear force.

5. The processing temperature of Parallel twin-screw extruder should keep between 240 ~ 260 ℃ with

vacuum at the same time.The temperature is too high, the physical property loss of PA66 is large, and the yellowing is also large.

6. Do not use low-alkali or high-alkali fiberglass. High-quality non-alkali fiberglass is preferred.

Package & Storage:

Net weight 25KG Kraft bag with PE liner.

It is not dangerous cargo .You should handle the material according to the instruction described on SDS.

Typical Application Data 1-1

Material	Formula 1	Formula 2	Formula 3	Formula 4
PA6	82	-	-	-
30%GF/PA6	-	84	-	-
PA66	-	-	82	-
30%GF/PA66	-	-	-	85
PN2131C	18	16	17	15

Properties 1-2

Item	Testing Method	Formula 1	Formula 2	Formula 3	Formula 4
UL94 (1.6mm)	UL94-2013	V-0	V-0	V-0	V-0
GWIT	IEC 60695-2-13	800°C	830°C	810°C	850°C
GWFI	IEC 60695-2-12	960°C	960°C	960°C	960°C
CTI	IEC60112	550 V	600 V	560 V	600 V
Tensile Strength	GB/T 1040.1-2006	64 Mpa	95 Mpa	78 Mpa	120 Mpa
Flexural Strength	GB/T 9341-88	85 Mpa	145 Mpa	125 Mpa	180 Mpa
Flexural modulus	GB/T 9341-88	2700 Mpa	5012 Mpa	4012 Mpa	7500 Mpa
Notch impact strength	GB/T 9342-88	13 KJ/m2	10 KJ/m2	11 KJ/m2	6.5 KJ/m2

Product Categories : Flame Retardant > Halogen-Free Flame Retardant

Hot Products

Email to this supplier

*Subject:
*To:

Mr. Ron Han
*Email:
*Message:

Your message must be between 20-8000 characters