ProFlame-PN6131 is formulated Flame Retardant based on organic P-Si component. It is suited for both
GF-reinforced and unreinforced PA66 and HTPA system. It exhibit high heat stability and no blooming.
Product benefits:
1. Less gas, less mold corrosion
2. Good machinability, no mold scale
3. Low dosage,Polyamide compounds show very good physical properties and excellent electrical properties
| | P-N system Proflame-PN2131 | P-P system Proflame-PN4131 | P-Si system Proflame-PN6131 |
| Migration resistance | ★ | ★★★ | ★★★ |
| Color Stability | ★★★ | ★★ | ★★ |
| Mechanical Performance | ★ | ★★ | ★★★ |
Technical Data:
Items Spec
Appearance White free-flowing powder
P content, % ≥19.0
Decomposition Temperature, °C ≥360
Average particle size, um 20-40
Moisture,% ≤0.5
Whiteness ≥95
Recommended dosage:
| Polymer | Dosage | UL-94 | GWIT | CTI |
| 30%GF-Reinforced PA66 | 12-18% | V0 (0.8-1.6mm) | 730°C (2mm) | 600V (4mm) |
Processing instruction:
1. Pre-drying the polyamide,the moisture content should be below 0.1 % (by wt.).
2. The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components.
3. Processing temperature: not more than 350°C. In PA66 with GF30 system, the recommended extrusion temperature is 245°C-265°C; In PA6 with GF30 system, the recommended temperature is 225°C - 250°C.
4. It is most suitable for equipment with weak shear force.
5. High-quality non-alkali fiberglass is preferred.
Net weight 25KG Kraft bag with PE liner.
Minimum shelf life is 12 months stored in a dry and ventilated warehouse.